Optimize Injection Molding Resins of PHA and PHA/PLA Blends

In the world of biobased and biodegradable injection molding resins, the newest kid on the block is polyhydroxyalkanoates (PHA). It has been used for extrusion for some time in the manufacture of straws and extrusion-coated paper, but injection molding grades are increasingly gaining traction.

Polylactic acid( PLA) and polylactic acid( PHA) can be used to create a bio-based and biomanufactured home compostable resin. In a fermentation process, various plant oils are fed to bacteria to create the PHA component. Phosphorus is a molecule that stores energy in the same way that body fat. The PHA is collected and purified after the bacteria have reached their maximum growth.

PHA is a fluffy white powder in its raw state that is not very useful for being converted into commercial goods. However, with current conversion procedures and processing aides or other biodegradable polyester resins like PLA, it becomes easier to manufacture products. In addition to cutlery, single-serve coffee pods, dental flossers, and children’s toys, the end-use applications of injection-molded PHA/PLA are biodegradable and compostable. Depending on a number of factors, the percentage of PHA in a PHA/PLA blend can vary significantly. These include the customer’s desired end-of-life( home compostable versus. performance considerations, cost, and marine degradability. The customer’s needs and how they intend to market their product will be taken into account when the product development team creates a specific blend. In most cases, the compounded resin will contain at least 50% PHA.

How To Optimize Injection Molding Resins of PHA and PHA/PLA Blends

PHA is similar to some existing resins, but also has its own unique characteristics. Because of its shear-creating nature, it can resemble PVC in its propensity to cause temperatures to overrun in the compression zone of the screw, and its flow characteristics make it seem like nylon in its propensity to flash at the smallest of parting line defects. By the very nature of being biodegradable, PHA is a somewhat fragile polymer, and excess heat, above 400°F, can cause rapid degradation. Even prolonged exposures to temperatures as low as 350°F will begin to degrade the material.

PHA is similar to some existing resins, but also has its own unique characteristics.

The processing of PHA resins in injection molding has its own rules, but is not overly complicated. Keep an eye on temperatures and residence times, keep the material dry, use a warm tool and you should be able to build a process to run your parts.

Key Considerations for Processing PHA and Blends

Most of the following processing guidelines are aimed at getting the resin into the process without degrading it, while others are aimed at reducing residence time at melt temperatures. The following guidance — for drying, purging and processing — relate to PHA resin but also to PHA blends, including PHA/PLA. As soon as you add even a modest percentage of PHA into a blend, its processing characteristics begin to dominate.

Injection molding resins Drying:

Because of the hygroscopic properties of PHA, drying before processing is required. A moisture content of less than 0.04% (400 ppm) is recommended to prevent viscosity degradation during processing. Recommended drying conditions are: four hours at not greater than 170°F (80°C) with a dew point of -40°F (-40°C), and an airflow rate greater than 0.5 cfm/lb of resin.

Injection molding resins Purging:

Before processing PHA, it is recommended that processing equipment be purged with LDPE (which has a low melting point) to remove any previous materials. This is followed by completely purging out the LDPE with the PHA material. This will also enable the PHA materials to remove the LDPE before processing begins. Purging with PP is not recommended unless LDPE is then used to remove any residual PP before transitioning to PHA materials. PHA can degrade quickly if left unattended within a heated barrel. Therefore, we recommend that any material left for longer than five minutes be purged with fresh material to ensure potentially degraded material is removed from the process. Recommended purging steps:

▪ Purge with LDPE at previous resin temperatures to remove any previous materials.

425-450°F (215-235°C)
LDPE with a 10-20 g/10 min MFI is recommended.
If applicable, purge hot runner with higher MFI LDPE (MFI target 18-20 range recommended).

▪ Decrease temperatures to 320-350°F (160-170°C), allow temps to stabilize at set point.

▪ Build process with LDPE to make full part.

After process has been established with LDPE, purge to PHA.

Process will be very close to LDPE with a longer cure time. (Reducing shot size slightly at start of PHA process is recommended to decrease chance of flashing or overpacking the tool.)

If machine is down for more than five minutes, purge 5-8 shots to clear out potentially degraded material before restarting.
If the machine will be down longer than 20-30 minutes, purge with LDPE to include hot runner; PHA degrades quickly and cannot be left in the barrel or hot runner for long periods of time.

Machine Setup and Hot Runner Systems

Here are suggested starting conditions and recommendations for hot runner systems. The ability to heat the mold is critical for proper performance of PHA. Inability to warm tool above ambient can result in decreased crystallization and poor processing rates.

▪ Starting conditions:

Feed Throat 310-330°F (155-165°C)

Feed Temp 320-340°F (160-170°C)

Compression Section 330-350°F (165-175°C)

Metering Section 320-340°F (160-170°C)

Nozzle 310-360°F (155-180°C)

Mold Temp 105-140°F (40-60°C)

▪ Hot runner systems:

If tool uses a hot runner system, we recommend setting temperatures as an extension of the nozzle. The hot runner should carry the material forward but not be used to add heat. Because these systems are designed for specific materials and tolerances, we always recommend reviewing upper and lower temperature limits with the manufacturer to avoid issues.

Overall Processing injection molding resins

The processing of PHA resins in injection molding has its own rules but is not overly complicated. Keep an eye on temperatures and residence times, keep the material dry, use a warm tool and you should be able to build a process to run your parts.

PHA-based resins are extremely sensitive to temperature changes, so great care should be taken to ensure recorded temperatures match set point temperatures upon transition to PHA resin. Starting at the lower range of temperature profile is recommended. Temperatures can be gradually increased, if needed, to enhance processing or improve product quality. Changes in set points to increase or decrease melt temperature should be small — think 2-3°- changes.

The ability to heat the mold is critical for proper performance of PHA.

Injection speeds should be as slow as possible to fill part to avoid shearing the material; hold times will be longer than seen with other common resins because of slower gate freeze times. The additional time can be subtracted from cure times. During extended runs, the material will off-gas similar to other resins, the easiest way to clean the vents and mold surfaces is with a rag dampened with warm water; most of the off-gas components are water soluble.

PHA resin is shear sensitive; some high-shear screws may cause reduction in material performance or viscosity. Low compression screws with standard general-purpose designs are recommended for this conversion process. Screw speeds should be set as slow as possible while remaining in cycle.